High-Strength Coating for Continuous Fiber 3D Printing
A material designed for coating composite fiber during continuous fiber coextrusion with the Anisoprint Composer 3D printer.
Reliable bonding of fiber layers and effective load distribution provide high strength characteristics for the resulting composite part.
The molecular structure and properties of the plastic help fill possible voids. Its low moisture absorption simplifies the process, allowing CFC PETG to be printed without the need for prior storing in a dry box.
PARAMETER | CCF-1.5K - PETG |
DENSITY, G/CM3 | 1.4 |
TENSILE STRENGTH ALONG PRINTING PATHS, MPA | 774 |
TENSILE MODULUS ALONG PRINTING PATHS, GPA | 57 |
TENSILE ELONGATION AT BREAK, % | 1.3 |
POISSON RATIO 21 | 0.4 |
COMPRESSIVE STRENGTH ALONG PRINTING PATHS, MPA | 237 |
COMPRESSIVE MODULUS ALONG PRINTING PATHS, GPA | 49 |
COMPRESSIVE ELONGATION AT BREAK, % | 0.52 |