Affordable and versatile
BigRep PLA’s strength and stiffness make it the ideal filament for demanding industrial production tasks, particularly in 3D printing large objects for architectural and construction applications. PLA can be effectively printed at lower to moderate temperatures and high speeds, and it exhibits minimal warping when compared to other polymers commonly used in 3D printing. Designed with BigRep’s large-scale 3D printers in mind, BigRep PLA allows for successful prints without the need for a specialized cooling system.
| PHYSICAL PROPERTIES: | |
Material: | BioPolymer |
Density (ISO 527): | 1.24 g/cm³ |
Filament Diameter: | 2.85 mm |
Color Availability: | Black, Grey, Natural, Orange, Purple, Red, White, Yellow |
Available Spool Sizes: | 2.5, 4.0 and 8.0 kg |
| MECHANICAL PROPERTIES: | |
Tensile Strength (ISO 527): | 60 MPa |
Tensile Modulus (ISO 527): | 3500 MPa |
Elongation at Break (ISO 527): | 4% |
Flexural Strength (ISO 178): | 80 MPa |
Flexural Modulus (ISO 178): | 3800 MPa |
Charpy Unnotched Impact Strength (ISO 179): | 7.5 kJ/m² |
Charpy Notched Impact Strength (ISO 179): | 2 kJ/m² |
| THERMAL PROPERTIES: | |
HDT B - 0.45 MPa (ISO 75): | 60°C |
HDT A - 1.8 MPa (ISO 75): | 55°C |
Glass Transition Temperature (Tg) (DSC): | 60°C |
Melting Temperature (DSC): | 155 - 160°C |